<address id="prxh1"></address>
<big id="prxh1"></big>
<delect id="prxh1"><listing id="prxh1"><output id="prxh1"></output></listing></delect>
<listing id="prxh1"></listing>
<track id="prxh1"></track>
<dl id="prxh1"><progress id="prxh1"><form id="prxh1"></form></progress></dl>
<pre id="prxh1"></pre>

<noframes id="prxh1"><span id="prxh1"><progress id="prxh1"></progress></span>

    <progress id="prxh1"></progress><listing id="prxh1"><span id="prxh1"></span></listing>
      <rp id="prxh1"><big id="prxh1"><th id="prxh1"></th></big></rp><rp id="prxh1"><delect id="prxh1"></delect></rp><noframes id="prxh1"><dfn id="prxh1"><address id="prxh1"></address></dfn><p id="prxh1"><big id="prxh1"></big></p>
      铁岭阀门制造有限公司

      新闻分类

      产品分类

      联系我们

      公司名称: 铁岭阀门制造有限公司

                (原名:铁岭阀门制造厂)

      电  话:024-72201228

      手  机:13804108883

      微  信:13804108883

      邮  件:Email: TLVF@163.com

      网  址:www.jamesfenimorecooper.com

      地  址:辽宁省铁岭市银州区工业园区

      本厂周六、周日不休息

      大口径阀门开关困难的解决方法

      您的当前位置: 首 页 >> 新闻中心 >> 行业新闻

      大口径阀门开关困难的解决方法

      发布日期:2019-08-13 作者: 点击:

       大口径阀门一般应用在锅炉出口、主分汽缸、蒸汽主管等位置,这些位置存在以下问题:

      1)、锅炉出口一般压差比较大,因此蒸汽流速也更大,对密封面的冲蚀破坏作用也较大。另外锅炉燃烧效率不可能为100%,这样将造成锅炉出口处的蒸汽含水量较大,容易对阀门密封面产生空化和汽蚀的破坏作用。

      2)、对锅炉出口及分汽缸附近的截止阀,因为刚从锅炉出来的蒸汽,有间断性过热现象发生,在其饱和的过程中,若锅炉水软化处理不是太好的话,往往会析出部分酸碱物质,对密封面会造成腐蚀和冲蚀;还有一些可结晶的物质也可能附着在阀门密封面结晶,导致阀门无法严密密封。

      3)、分汽缸进出口阀门,因阀后蒸汽用量因生产要求等原因而造成用汽量时大时小,在流速变化较大的情况下,很容易产生闪蒸、空化等现象,从而对阀门密封面造成冲蚀、汽蚀等破坏作用。

      4)、一般大管径管线开启时,都需要对管线进行预热,而预热过程一般要求很小流量蒸汽通过,使管线缓慢均匀加热到一定程度后,才能完全开启截止阀,避免造成管线急速升温而产生过度膨胀,损坏部分连接部位。但在这过程中,阀门开度往往非常小,从而造成冲蚀率远远大于正常使用效果,严重降低阀门密封面的使用寿命。

      大口径阀门

      大口径截止阀开关困难解决方法

      1)、首先建议选择波纹管密封截止阀,避免了柱塞阀、填料阀摩擦阻力影响,开关更轻松。

      2)、阀芯阀座一定要选择耐冲蚀、磨损性能好的材质,如司太立硬质合金;

      3)、建议采用双阀瓣结构,不因小开度而造成过度冲蚀,影响使用寿命及密封效果。

      文章内容来源于网络,如有问题,请与我们联络!